Rigid Materials
- Tensile Strength: 40-55 MPa
- Flexural Strength: 70-110 MPa
- Impact Resistance (Izod): 30-60 J/m
- HDT: 60-90°C (at 0.455 MPa)
- Thermal Conductivity: 0.13-0.19 W/mK
- Elongation at Break: 10-40%
- Modulus of Elasticity: 2500-
- 4000 MPa
- Shore Hardness: 75-85 (Shore D)
- Excellent Thermal Insulating Properties
- Ultra Low Coefficient of Linear Thermal Expansion
- Excellent Silicone Adhesion
- Dow Corning Tested and Approved for use with Dow Silicone Sealants
- Newest Product
- Tensile Strength: 48-60 MPa
- Flexural Strength: 80-110 MPa
- Impact Resistance (Izod): 60-150 J/m
- HDT: 90-110°C (at 0.455 MPa)
- Thermal Conductivity: 0.14-0.18 W/mK
- Elongation at Break: 10-25%
- Modulus of Elasticity: 2200-2700 MPa
- Shore Hardness: 80-95 (Shore D)
- Tensile Strength: 25-40 MPa
- Flexural Strength: 30-50 MPa
- Impact Resistance (Izod): 30-80 J/m
- HDT: 50-100°C (at 0.455 MPa)
- Thermal Conductivity: 0.20-0.30 W/mK
- Elongation at Break: 200-800%
- Modulus of Elasticity: 1000-1800 MPa
- Shore Hardness: 70-80 (Shore D)
- Tensile Strength: 30-50 MPa
- Flexural Strength: 50-100 MPa
- Impact Resistance (Izod): 10-20 J/m
- HDT: 70-100°C (at 0.455 MPa)
- Thermal Conductivity: 0.12-0.18 W/mK
- Elongation at Break: 1-3%
- Modulus of Elasticity: 2000-3000 MPa
- Shore Hardness: 85-100 (Shore D)
- Tensile Strength: 40-55 MPa
- Flexural Strength: 65-85 MPa
- Impact Resistance (Izod): 200-300 J/m
- HDT: 85-105°C (at 0.455 MPa)
- Thermal Conductivity: 0.17-0.20 W/mK
- Elongation at Break: 10-50%
- Modulus of Elasticity: 2000-2400 MPa
- Shore Hardness: 95 (Shore D)
- Tensile Strength: 20-35 MPa
- Flexural Strength: 20-30 MPa
- Impact Resistance (Izod): 100-160 J/m
- HDT: 45-80°C (at 0.455 MPa)
- Thermal Conductivity: 0.42-0.52 W/mK
- Elongation at Break: 500-800%
- Modulus of Elasticity: 800-1400 MPa
- Shore Hardness: 60-70 (Shore D)
- Tensile Strength: 60-75 MPa
- Flexural Strength: 90-110 MPa
- Impact Resistance (Izod): 15-25 J/m
- HDT: 90-105°C (at 0.455 MPa)
- Thermal Conductivity: 0.17-0.20 W/mK
- Elongation at Break: 2-5%
- Modulus of Elasticity: 2800-3200 MPa
- Shore Hardness: 80-95 (Shore D)
- Tensile Strength: 20-30 MPa
- Flexural Strength: 20-35 MPa
- Impact Resistance (Izod): 150-200 J/m
- HDT: 50-70°C (at 0.455 MPa)
- Thermal Conductivity: 0.35-0.45 W/mK
- Elongation at Break: 400-700%
- Modulus of Elasticity: 700-1000 MPa
- Shore Hardness: 60-65 (Shore D)
- Tensile Strength: 55-75 MPa
- Flexural Strength: 85-120 MPa
- Impact Resistance (Izod): 600-850 J/m (Notched)
- HDT: 120-140°C (at 0.455 MPa)
- Thermal Conductivity: 0.19-0.22 W/mK
- Elongation at Break: 100-150%
- Modulus of Elasticity: 2000-2400 MPa
- Shore Hardness: 75-85 (Shore D)
Capstock Materials
- Flexural Strength: 90-110 MPa
- Impact Resistance (Izod): 15-25 J/m (Notched)
- Modulus of Elasticity: 2800-3200 MPa
- Shore Hardness: 80-95 (Shore D)
- Flexural Strength: 55-80 MPa
- Impact Resistance (Izod): 150-300 J/m (Notched)
- Modulus of Elasticity: 1600-2300 MPa
- Shore Hardness: 85-95 (Shore D)
Flexible Materials
- Tensile Strength: 10-25 MPa
- Thermal Conductivity: 0.14-0.17 W/mK
- Elongation at Break: 200-450%
- Shore Hardness: 60-90 (Shore A)
- Tensile Strength: 5-20 MPa
- Thermal Conductivity: 0.15-0.20 W/mK
- Elongation at Break: 200-800%
- Shore Hardness: 20-90 (Shore A)
- Tensile Strength: 6-18 MPa
- Thermal Conductivity: 0.16-0.18 W/mK
- Elongation at Break: 300-550%
- Shore Hardness: 35-95 (Shore A)
- Tensile Strength: 25-50 MPa
- Thermal Conductivity: 0.20-0.25 W/mK
- Elongation at Break: 300-700%
- Shore Hardness: 40-72 (Shore D)